Page Title:
Figure 1. Heat cycle for dimensional stability test |
|
||
| ||||||||||
|
|  MIL-P-47099A
15 HR.
∫∫
+155F
40%
HUMIDITY
AMBIENT (ROOM)
+32F
HUMIDITY
NOT
CONTROLLED
∫∫
-65F
1.5 HR.
3 HR.
3 HR.
1.5 HR.
24 HR.
2 CYCLE
FIGURE 1.
Heat cycle for dimensional stability test.
4.7.9 Flammability. The material shall be tested in accordance with
MIL-F-83671 for conformance to table I.
4.7.10 Temperature resistance. The material shall be baked for a period which
shall be not less than one hour at 86.9 3C(190 5F) for conformance to table I.
4.7.11 Humidity growth. The material shall be tested in accordance with MIL-
STD-810, Method 507, for conformance to table I.
4.7.12 Fungus resistance. The material shall be tested in accordance with
MIL-STD-810, Method 508, for conformance to table I.
5. PACKAGING
5.1 Preservation. Preservation shall be levels A, B or C (see 6.2).
5.1.1 Level A.
5.1.1.1 Unit packs. The polyether type polyurethane base resin and a separate
isocyanate-type curing agent shall be unit packed in accordance with MIL-P-116,
method IA-5. The polyether type polyurethane base resin and the isocyanate-type
8
|
|