|  MIL-S-1399E(AR)
2.2 Other publications. The following documents form a part of
this specification to the extent specified herein. The issue of the
document which are indicated as DOD adopted shall be the issue
listed in the current DODISS and the supplement thereto, if
applicable.
AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM)
- Recommended Practice for Sampling
ASTM Designation E300
Industrial Chemicals
(Applications for copies should be addressed to the American
Society for Testing Materials, 1916 Race Street, Philadelphia, PA
19103) l
2.3 Order of precedence. In the event of a conflict between
the text of this specification and the references cited herein, the
text of this specification shall take precedence.
REQUIREMENTS
3.
3.1 Material. Material and parts shall be in accordance with
the applicable drawings and specifications.
3.2 Assembly. The assembly shall comply with all requirements
specified on Drawing (dwg.) 8847441 and with all requirements
specified in applicable specifications.
3.3 Moisture content.
3.3.1 Star charge composition. The moisture content of the
star charge composition, at the loading station shall not exceed 0.1
percent when determined as specified in 4.5.1.1 or 4.5.1.2.
3.3.2 Tracer charge composition. The moisture content of the
tracer charge composition, at the time of loading the signals, shall
not exceed 0.1 percent when determined as specified in 4.5.1.2.
3.3.3 Black powder. The moisture content of the black powder,
at the loading station at the time of loading the signals shall not
exceed 0.3 perecent when determined as specified in 4.5.1.3.
3.3.4 Paper, cotton and chipboard components. The moisture
content of the paper, cotton and chipboard components, at the
loading station at the time of loading the signals, shall not exceed
6 percent when determined as specified in 4.5.1.4.
3.3.5 Polypropylene felt. The moisture content of the
polypropylene felt components, at the loading station at the time of
loading shall not exceed 0.1 percent when determined as specified in
4.5.1.4.