Page Title:
Table II. First article testing |
|
||
| ||||||||||
|
|  MILL87177A
TABLE II. First article testing l/
Characteristics
Requirements
Test method
ASTM
Dryness
3.3, table I
4.6.1
Flash point
3.3, table I
D1310
Grade A synthetic
3.3, table I
4.6.2
sea water
displacement
Dielectric breakdown
3.3, table I
D877
Lubricity
3.3, table I
D2266 2/
Residue soluble in
3.3, table I
4.6.3
trichlorotrifluoroethane
Leakage
3.4.1.1
4.6.4
Content
3.4.1.2
4.6.5
Performance of
3.4.1.2
4.6.6
pressurized containers
Oxidation stability
3.3, table I
D942
Grade A corrosivity
3.4.3
4.6.7
Grade B corrosion
3.4.4
4.6.8
resistance
Sprayability
3.3, table I
4.6.9
Grade C shall meet all the first article testing in table II, except the corrosivity (Grade
A) and corrosion resistance (Grade B) requirements.
1/
Refer to 4.3.1
2/
Compound shall be weathered before loading into ball pot.
4.5.2 Sampling Plan B. A random sample of type I filled containers shall be selected in
accordance with MILSTD105, inspection level I with an AQL 2.5 percent defective
from each inspection lot (see 4.3.3). The sample container(s) shall be subjected to the
tests specified in table II.
4.5.3 Certification. The manufacturer shall certify that there has been no formulation or
process change from that which resulted in the production of the first article inspection
sample(see 4.4.2). Each ingredient material shall be identified with the name of its
manufacturer and that manufacturer's trade name and formula number.