Environmental tests of components |
|
||
| ||||||||||
|
|  MIL-M-81752A(AS)
4.3.3.5 - Color - If polycarbonate material is used in windshield
construction, color of the core ply mill run shall be tested in
accordance with ASTM D-1925 to show conformance with 3.8.6.12 herein.
4.3.4 - Environmental tests of components - Components shall be
subjected to the following environmental tsts specified in MIL-STD-
Failure to pass specified tests shall be cause for rejection.
810.
High temperature test, Method 501.1.
a.
b.
Temperature-altitude, Method 504.1.
LoW temperature test, Method 502.1.
c.
Temperature shock, Method 503.1
d.
Humidity test, Method 507.1.
e.
Solar radiation (sunshine), Method 505.1.
f.
Altitude test, Method 500.1.
g.
Rain, Method 506.1.
h.
i.
Salt spray test, Method 509.1.
Vibration test, Method 514.2.
j.
Fungus resistance test, Method 508.1.
k.
l.
Sand and dust test, Method 510.1.
Acceleration test, Method 513.2.
m.
Shock test, Method 516.2.
n.
4.3.4.1 - Additional tests - The windshield transparency shall
also be subjected to the following tests. Failure to pass specified
tests shall be cause for rejection.
Crazing resistance tests in accordance with FTM-406
a.
Method 6053.
No crazing of the transparent material
shall be allowed.
b.
Hail impact tests per ASTM F-320.
4.4 - Acceptance tests
19
|
|